Yleispigmentit, As Powder

Firing range 920 - 1300°C. Chemical composition Zr-Si-Pr.
Optimal amount when added to glaze approx. 3 - 6%. 

Firing range 920 - 1400°C. Chemical composition Zr-Si-Pr-V.
Optimal amount when added to glaze approx. 3 - 6%. 

Firing range 920 - 1300°C. Chemical composition Zr-Si-Cd-S-Se.
Optimal amount when added to glaze approx. 8 - 10%. Tähdellä merkityt... 

Firing range 920 - 1350°C. Chemical composition Cr.
Optimal amount when added to glaze approx. 3 - 6%. 

Firing range 920 - 1350°C. Chemical composition Cr-Co-Al-Zn.
Optimal amount when added to glaze approx. 3 - 6%. 

Firing range 920 - 1250°C. Chemical composition Zr-Si-Pr-V.
Optimal amount when added to glaze approx. 6%. 

Firing range 920 - 1250ºC. Chemical composition Cr-Sn-Ca-Si
Optimal amount when added to glaze approx. 10%. On some glazes the pigment may lose... 

Firing range 920 - 1250°C. Chemical composition Cr-Sn-Ca-Si
Optimal amount when added to glaze approx. 10%. On some glazes the pigment may lose... 

Max. temperature 1250ºC. Chemical composition Sn-Cr.
Optimal amount when added to glaze approx. 10%. On some glazes the pigment may lose its colour... 

Firing range 920 - 1300°C. Chemical composition Zr-Si-Cd-S-Se.
Optimal amount when added to glaze approx. 8 - 10%. Tähdellä merkityt... 

Co-Si
920º-1250ºC
Hyvin tumma koboltinsininen pigmentti. 

Firing range 920 - 1300°C. K2269=26/9
Chemical composition Sn-Sb.
Optimal amount when added to glaze approx. 5... 

Firing range 920 - 1240°C. K2278=27/8
Chemical composition Sn-Ca-Si-Cr. Vaaleammassa munassa 8% pigmenttiä on lisätty transparenttiin mattalasitteeseen ja... 

Code K2291 has been replaced with K2709. Firing range 920 - 1300°C. Upper piece fired at 1255°C and lower at 1050°C.
Molemmissa lasitepohjana on... 

Firing range 920 - 1300°C. K2297=29/7
Chemical composition Cr-Co.
Optimal amount when added to glaze approx. 5%. Kuvassa... 

Firing range 920 - 1300°C. K2317=31/7
Chemical composition Zr-Si-V
Optimal amount when added to glaze approx. 5... 

Firing range 920 - 1300°C. K2323=32/3
Chemical composition Zr-V
Optimal amount when added to glaze approx. 5... 

Firing range 920 - 1300°C. K2324=32/4
Upper piece fired at 1020°C and lower at 1250°C.
Molemmissa lasitepohjana on...