Firing range 920 - 1300°C.
K2324=32/4
Upper piece fired at 1020°C and lower at 1250°C.
Molemmissa lasitepohjana on kirkas laajapolttoinen 921 lasite ja pigmenttiä lisätty 8%.
K2324 Blue-Grey
Main Page > Värituotteet > Yleispigmentit, As Powder > Yleispigmentit Cerama / R&S, max 1300ºC
See also
Firing range 920 - 1250°C. Chemical composition Zr-Si-Pr-V.
Optimal amount when added to glaze approx. 6%.
Optimal amount when added to glaze approx. 6%.
from
11,00 €
Firing range 920 - 1300°C. K2323=32/3
Chemical composition Zr-V
Optimal amount when added to glaze approx. 5...
Chemical composition Zr-V
Optimal amount when added to glaze approx. 5...
from
14,57 €
Firing range 920 - 1350°C. Chemical composition Al-Co-Ni-Zn.
Optimal amount when added to glaze approx. 5%.
Optimal amount when added to glaze approx. 5%.
from
6,00 €
0 - 0,5mm with 40% chamotte. See technical data here. Firing range 1000 - 1260ºC.
Clay with fine grained grog 40% is excellent for tiles and other...
Clay with fine grained grog 40% is excellent for tiles and other...
from
11,12 €
/kg
Firing range 920 - 1350°C. Chemical composition Cr-Co-Si.
Optimal amount when added to glaze approx. 3 - 6%.
Optimal amount when added to glaze approx. 3 - 6%.
from
6,00 €
Code K2291 has been replaced with K2709. Firing range 920 - 1300°C. Upper piece fired at 1255°C and lower at 1050°C.
Molemmissa lasitepohjana on...
Molemmissa lasitepohjana on...
from
5,77 €
Firing range 920 - 1300°C. Chemical composition Zr-Si-Cd-S-Se.
Optimal amount when added to glaze approx. 8 - 10%. Tähdellä merkityt...
Optimal amount when added to glaze approx. 8 - 10%. Tähdellä merkityt...
from
14,00 €